Triple Coatings & Other Coating Structures | Advanced Coating Service

triple coating

What is meant by the term “triple coatings”?

“TripleCoatings®” is a term coined by Platit, a Swiss manufacturer of PVD coating equipment, to identify a new generation of coating structures that they introduced in 2007. They specifically designed their cathodic arc coating unit “Pi311” to utilize 4 targets inside of the coating chamber to produce the TripleCoating3®.

3 THIN FILM LAYERS

The film structure consists of 3 thin film layers that are stacked on top of each other (like two slices of bread surrounding a filling to make a sandwich). The initial layer that is applied after the metal ion etching of the substrate is a layer that promotes adhesion. The middle layer of the sandwich is a thicker core layer that is grown in either the Monoblock or Gradient film structure. The top, or “capping,” layer is then deposited as a thin nanocomposite film structure

COATING STRUCTURES

Let’s break down the different coating structures and describe them in more detail.

triple coating

MONOBLOCK COATING STRUCTURE

The Monoblock Structure is the simplest structure. All of the targets are the same, and they run continuously during the deposition steps.

monoblock coating structure

 

MULTILAYER COATING STRUCTURE

The Multilayer Structure has a “sandwich” structure which achieves a higher toughness at a lower hardness than a monoblock coating structure. Another key benefit of the “sandwich” structure is that any microcracks that develop during use are contained within the layer where they occur, instead of spreading all of the way through the film.

multilayer coating structure

GRADIENT COATING STRUCTURE

The Gradient Structure begins with a CrN or TiN adhesion layer. Next, it is overcoated with a constantly varying ratio of metallic elements. This occurs so that the film exhibits maximum toughness at its core, and the highest hardness towards the top of the coating layer. The gradient in the image of the film above is visually indicated by the slight color shift. Notice the shift from the top to the bottom arc, where the color has turned white and yellow.

gradient coating structure

NANOLAYER COATING STRUCTURE

The Nanolayer Structure is a “finer structure” version of the multilayer structure; that is, the layers are much thinner than the layers in the multilayer structure. The layer thickness is controlled by varying the rotational speed of the fixtures inside of the chamber. This film structure is used to form the family of coatings called “nanocoatings”.

nanolayer coating structure

NANOCOMPOSITE COATING STRUCTURE

The Nanocomposite Structure is a huge performance benefit in the world of hard coatings. The deposition process is controlled in a way that prevents the deposition materials from mixing into a single compound during the coating. Two distinct film phases are formed. Therefore, if targets of Ti, Al, and Si are used in a nitrogen background, then TiAlN grains are formed which become embedded in the Si3N4 amorphous film that is growing simultaneously. This is the nACo coating, or AlTiN/Si3N4. Likewise, if targets of Cr, Al, and Si are used in a nitrogen background, then AlCrN grains are formed which become embedded in the Si3N4 amorphous film that is growing simultaneously. This is the nACRO coating, or AlCrN/Si3N4.

nanocomposite coating structure

TRIPLE COATING STRUCTURE

Now that the individual coating structures have been further defined, here is a review of the TripleCoating structure and how the various structures described above are combined to form the revolutionary TripleCoatings.

TRIPLE COATING LAYERS

TripleCoatings®, a series of Platit trademarked structures, were developed as premium coatings for demanding machining applications. They utilize 3 distinct layer structures to produce an optimized film structure of three stacked layers that are strongly bonded to each other.

LAYER 1: ADHESION

They begin with an adhesion layer of TiN or CrN that is about 2,000 to 5,000 angstroms thick, and is tenaciously bonded to the surface of the tool.

LAYER 2: TOUGHNESS

Next is a thicker “core” layer that is of the Monoblock or Gradient coating structure. It provides the high toughness that a stacked structure provides. In most circumstances, this core layer is either AlTiN (for nACo) or AlTiCrN (for nACRo). This layer bonds well to the TiN or CrN adhesion layer.

LAYER 3: HARDNESS, TOUGHNESS, & HEAT RESISTANCE

Finally, a thin nanocomposite layer is applied within the same chamber pumpdown to act as an extremely hard and wear resistant topcoat. This topcoat, or “capping layer,” has a unique structure in which very hard TiAlN (for the nACo film) or AlCrN (for the nACRo film) grains are embedded into an amorphous silicon nitride (Si3N4) matrix that limits the encapsulated grain size. This layer exhibits extremely high nanohardness at very high toughness, and provides extremely high heat resistance.

TRIPLE COATING PROCESS

By deposition of very different kinds of materials, the components (like Ti, Cr, Al in the first group, and Si in the second group) are not mixed completely, and 2 material phases are created. The nanocrystalline TiAlN or AlCrN grains become embedded in the amorphous Si3N4 matrix and the nanocomposite top structure develops. Silicon is added to the composition to increase the toughness and decrease the internal residual stress of the coating. The increasing hardness is generated by the film structure only. The softer amorphous Silicon Nitride matrix enwraps the hard grains and the increasing Si content changes the structure from columnar to isotropic.

TRIPLE COATING BENEFITS

The TripleCoatings are especially useful when machining “difficult to cut” materials, highly alloyed steels, and superalloys. The introduction of the TripleCoatings allowed technical and functional improvements in the nACo and nACRo films that ACS offers.

HOW NACO & NACRO BECAME 3-LAYERED STRUCTURES

Originally, when nACo (also designated as nACo2 or nACo®) was introduced by Platit on earlier generation coating machines, it was offered as a simple nanocomposite coating. It was a single layer structure of AlTiN grains in the Si3N4 amorphous matrix. Once the TripleCoating® technology was developed in conjunction with the Pi311 system, the name was modified to nACo3® or nACo3, and became the 3-layered structure described earlier, consisting of TiN + AlTiN + TiAlN/Si3N4. The same thing happened with Platit’s original nACRo (also nACRo2 or nACRo®). This nanocomposite coating from the earlier coating machines consisted of a single layer structure of AlCrN grains in the Si3N4 amorphous matrix. With the use of TripleCoating® technology that was released with the Pi311, this coating became a 3-layered structure known as nACRo3® or nACRo3, which consists of CrN + AlTiCrN + AlCrN/Si3N4.

WHY CHOOSE TRIPLE COATING?

Are triple coatings worth the price premium? That depends on your application and the cost of your tooling, machine setup, and downtime. If you are a tool regrinding provider, and are not stripping the old coatings off the tool before the regrinding operation, then TripleCoating is most likely not cost effective. Conversely, if you have a high value tool that is to be used against a difficult to machine substrate, a TripleCoating could be the solution to incrementally improve an optimized tool design. If you think you have an application that might benefit from this revolutionary coating structure, please contact us to discuss your specific project.